Silicon rubber for magnesium oxide mould
summary
Silicon rubber for iron oxide mould is a two-component condensation type silicon rubber.
It contains two components, A as the main agent and B as the curing agent. After the two solutions are mixed, they can be cured at room temperature for rapid prototyping.
characteristic
1. Good fluidity, easy to bubble, easy to demould and easy to process.
2. It is easy to apply color without peeling off paint.
3. Excellent tensile strength and tear strength, not easy to deform.
application
Magnesium oxide flowerpots, magnesium oxide handicrafts and other products.
Product parameters：
Processing program
1. Take the required amount of component A and put it into a container 3-4 times larger, and add the weight ratio according to the product parameter table
The components shall be fully stirred and mixed evenly, and then can be used after vacuum deaeration.
2. The ideal operating environment for this product is 20-25 ° C and 50% relative humidity. High temperature and high humidity or low temperature and low humidity will affect the gelling time and curing time, so it is necessary to adjust the amount of curing agent to achieve the expected results.
storage
To ensure the good quality of this product, it should be stored in a dry environment with room humidity of 25 ℃ and in a sealed container.
Conventional packaging
Packed in 25kg drums or 200kg drums.